Electrochromic device having a current-reducing additive

ABSTRACT

An electrochromic medium for use in an electrochromic device comprising: at least one solvent; an anodic electroactive material; a cathodic electroactive material, wherein at least one of the anodic and cathodic electroactive materials is electrochromic; and a current-reducing additive, wherein the current-reducing additive comprises a polymer present in an effective concentration to materially reduce the current of the electrochromic medium upon application of an electrical potential, relative to an electrochromic medium without the current-reducing additive, while maintaining an electrochromic medium viscosity which facilitates acceptable production rates without a problematic degree of seal or other device component failure.

This application is a continuation application of U.S. application Ser.No. 10/372,073 filed on Feb. 21, 2003 U.S. Pat. No. 6,778,311, which isa continuation application of U.S. application Ser. No. 10/012,937 filedon Dec. 10, 2001, now U.S. Pat. No. 6,525,861 B1, the entirety of whichare hereby incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates in general to electrochromic devices, andmore particularly, to an electrochromic medium for use in anelectrochromic device which includes a current-reducing additivecomprising a polymer present in an effective concentration to materiallyreduce the current of the electrochromic medium upon application of anelectrical potential, relative to an electrochromic medium without thecurrent-reducing additive, while maintaining a sufficiently lowviscosity to facilitate acceptable production rates without aproblematic degree of seal or other device component failure.

2. Background Art

Electrochromic devices have been known in the art for several years.While the utilization of electrochromic devices, such as electrochromicmirrors, has become increasingly popular, for example, among theautomotive industry, the operating current of many electrochromicdevices remains problematic for a plurality of reasons.

For example, one problem associated with electrochromic devices which,at least in part, can be attributed to current or electron flow is theformation of color bands proximate the electrodes of the electrochromicdevice, which is commonly referred to as “segregation.” Segregation canbe especially prevalent after an electrochromic device is held in a lowtransmission or colored state for an extended period of time.Electrochromic windows are very susceptible to segregation inasmuch as,during normal operation, they may remain in a colored state for several,continuous hours.

A second problem associated with electrochromic devices that is directlyrelated to current is that the electrochromic devices can generate asubstantial amount of heat upon application of an electrical potential.The generated heat can, in turn, impart undesirable stress upon many ofthe electrical components used to control the electrochromic device.Often times, this requires many of the electrical components to bespecially designed to handle extreme temperature variations for extendedperiods of time, which can materially increase the cost of theelectrochromic device.

A third problem associated with electrochromic devices that is directlyrelated to current is that the electrochromic devices can require asubstantial draw of power during normal operation, which is a materialconcern with large area electrochromic devices, such as large exteriorelectrochromic mirrors for automobiles or electrochromic windows forresidential, commercial, and/or industrial buildings.

One attempt to reduce current is disclosed in U.S. Pat. No. 5,142,407(hereinafter the '407 patent). The '407 patent teaches incorporatingcyanoethylsucrose (hereinafter “CES”), a non-polymer, into anelectrochromic medium to reduce leakage current. However, theincorporation of CES into an electrochromic medium is undesirable for aplurality of reasons, including, but not limited to, the fact that CEScan be costly, especially at the loading concentrations required tomaterially reduce leakage current. Moreover, the incorporation of anadditive in such high concentrations may raise issues relative to thelong term performance, stability, and/or operation of an associatedelectrochromic device.

It is therefore an object of the present invention to provide anelectrochromic device which utilizes one or more relatively common andinexpensive low molecular weight polymers as current-reducing additivesthat remedy, or at least minimize, the aforementioned detriments and/orcomplications associated with the operating current of many presentlyavailable electrochromic devices while maintaining a sufficiently lowviscosity to facilitate acceptable production rates without aproblematic degree of seal or other device component failure.

In addition, if an electrochromic device is operating at an acceptablecurrent, the incorporation of one or more additives of the presentinvention can enable an electrochromic device to be reconfigured with asmaller cell spacing while maintaining a generally constant current.Electrochromic devices having reduced cell spacing are beneficial for atleast three reasons. First, electrochromic devices having reduced cellspacing can more easily achieve an acceptable image or viewing quality,especially for large-scale electrochromic devices. Second,electrochromic devices having reduced cell spacing contain lesselectrochromic medium, and, accordingly, have an inherently lower cost.They also weigh less, which can be important for small scale, mobile,and/or weight sensitive applications. Third, electrochromic deviceshaving reduced cell spacing can be manufactured with increasedefficiency.

These and other objectives of the invention will become apparent inlight of the present specification, claims, and drawings.

SUMMARY OF THE INVENTION

The present invention is directed to an electrochromic medium for use inan electrochromic device comprising: (a) at least one solvent; (b) ananodic electroactive material; (c) a cathodic electroactive material,wherein at least one of the anodic and cathodic electroactive materialsis electrochromic; and (d) a current-reducing additive, wherein thecurrent-reducing additive comprises a polymer present in an effectiveconcentration to materially reduce the current of the electrochromicmedium upon application of an electrical potential, relative to anelectrochromic medium without the current-reducing additive, whilemaintaining a sufficiently low viscosity to facilitate acceptableproduction rates without a problematic degree of seal or other devicecomponent failure.

The present invention is also directed to an electrochromic devicecomprising: (a) a first substantially transparent substrate having anelectrically conductive material associated therewith; (b) a secondsubstantially transparent substrate having an electrically conductivematerial associated therewith; and (c) an electrochromic mediumcontained within a chamber positioned between the first and secondsubstrates which comprises: (1) at least one solvent; (2) an anodicelectroactive material; (3) a cathodic electroactive material, whereinat least one of the anodic and cathodic electroactive materials iselectrochromic; and (4) a current-reducing additive, wherein thecurrent-reducing additive comprises a polymer present in an effectiveconcentration to materially reduce the current of the electrochromicmedium upon application of an electrical potential, relative to anelectrochromic medium without the current-reducing additive, whilemaintaining a sufficiently low viscosity to facilitate acceptableproduction rates without a problematic degree of seal or other devicecomponent failure.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will now be described with reference to the drawingswherein:

FIG. 1 of the drawings is a cross-sectional schematic representation ofan electrochromic device fabricated in accordance with the presentinvention;

FIG. 2 of the drawings is a plot showing change in current as a functionof current-reducing additive concentration for Experiment No. 1;

FIG. 3 of the drawings is a plot showing change in current as a functionof current-reducing additive concentration for Experiment No. 2;

FIG. 4 of the drawings is a plot showing change in current as a functionof current-reducing additive concentration for Experiment No. 3;

FIG. 5 of the drawings is a plot showing change in current as a functionof current-reducing additive concentration for Experiment No. 4; and

FIG. 6 of the drawings is a plot showing change in viscosity as afunction of current-reducing additive concentration for a plurality ofcurrent-reducing additives provided herein.

DETAILED DESCRIPTION OF THE INVENTION

Referring now to the drawings and to FIG. 1 in particular, across-sectional schematic representation of electrochromic device 100 isshown, which generally comprises first substrate 112 having frontsurface 112A and rear surface 112B, second substrate 114 having frontsurface 114A and rear surface 114B, and chamber 116 for containingelectrochromic medium 124. It will be understood that electrochromicdevice 100 may comprise, for illustrative purposes only, a mirror, awindow, a display device, a contrast enhancement filter, and the like.It will be further understood that FIG. 1 is merely a schematicrepresentation of electrochromic device 100. As such, some of thecomponents have been distorted from their actual scale for pictorialclarity. Indeed, numerous other electrochromic device configurations arecontemplated for use, including those disclosed in U.S. Pat. No.5,818,625 entitled “Electrochromic Rearview Mirror Incorporating A ThirdSurface Metal Reflector” and U.S. Pat. No. 6,597,489 entitled “ElectrodeDesign For Electrochromic Devices,” both of which are incorporatedherein by reference in their entirety.

First substrate 112 may be fabricated from any one of a number ofmaterials that are transparent or substantially transparent in thevisible region of the electromagnetic spectrum, such as, for example,borosilicate glass, soda lime glass, float glass, natural and syntheticpolymeric resins, plastics, and/or composites including Topas®, which iscommercially available from Ticona of Summit, N.J. First substrate 112is preferably fabricated from a sheet of glass having a thicknessranging from approximately 0.5 millimeters (mm) to approximately 12.7mm. Of course, the thickness of the substrate will depend largely uponthe particular application of the electrochromic device. Whileparticular substrate materials have been disclosed, for illustrativepurposes only, it will be understood that numerous other substratematerials are likewise contemplated for use—so long as the materials areat least substantially transparent and exhibit appropriate physicalproperties, such as strength to be able to operate effectively inconditions of intended use. Indeed, electrochromic devices in accordancewith the present invention can be, during normal operation, exposed toextreme temperatures as well as substantial UV radiation, emanatingprimarily from the sun.

Second substrate 114 may be fabricated from similar materials as that offirst substrate 112. However, if the electrochromic device is a mirror,then the requisite of substantial transparency is not necessary. Assuch, second substrate 114 may, alternatively, comprise polymers,metals, glass, and ceramics—to name a few. Second substrate 114 ispreferably fabricated from a sheet of glass having a thickness rangingfrom approximately 0.5 mm to approximately 12.7 mm. If first and secondsubstrates 112 and 114, respectively, are fabricated from sheets ofglass, then the glass can optionally be tempered prior to or subsequentto being coated with layers of electrically conductive material (118 and120).

One or more layers of electrically conductive material 118 areassociated with rear surface 112B of first substrate 112. These layersserve as an electrode for the electrochromic device. Electricallyconductive material 118 is desirably a material that: (a) issubstantially transparent in the visible region of the electromagneticspectrum; (b) bonds reasonably well to first substrate 112; (c)maintains this bond when associated with a sealing member; (d) isgenerally resistant to corrosion from materials contained within theelectrochromic device or the atmosphere; and (e) exhibits minimaldiffuse or specular reflectance as well as sufficient electricalconductance. It is contemplated that electrically conductive material118 may be fabricated from fluorine doped tin oxide (FTO), for exampleTEC glass, which is commercially available from Libbey Owens-Ford-Co.,of Toledo, Ohio, indium/tin oxide (ITO), doped zinc oxide or othermaterials known to those having ordinary skill in the art.

Electrically conductive material 120 is preferably associated with frontsurface 114A of second substrate 114, and is operatively bonded toelectrically conductive material 118 by sealing member 122. As can beseen in FIG. 1, once bonded, sealing member 122 and the juxtaposedportions of electrically conductive materials 118 and 120 serve todefine an inner peripheral geometry of chamber 116.

Electrically conductive material 120 may vary depending upon theintended use of the electrochromic device. For example, if theelectrochromic device is a mirror, then the material may comprise atransparent conductive coating similar to electrically conductivematerial 118 (in which case a reflector is associated with rear surface114B of second substrate 114). Alternatively, electrically conductivematerial 120 may comprise a layer of reflective material in accordancewith the teachings of previously referenced and incorporated U.S. Pat.No. 5,818,625. In this case, electrically conductive material 120 isassociated with front surface 114A of second substrate 114. Typicalcoatings for this type of reflector include chromium, rhodium,ruthenium, silver, silver alloys, and combinations thereof.

Sealing member 122 may comprise any material that is capable of beingadhesively bonded to the electrically conductive materials 118 and 120to, in turn, seal chamber 116 so that electrochromic medium 124 does notinadvertently leak out of the chamber. As is shown in dashed lines inFIG. 1, it is also contemplated that the sealing member extend all theway to rear surface 112B and front surface 114A of their respectivesubstrates. In such an embodiment, the layers of electrically conductivematerial 118 and 120 may be partially removed where the sealing member122 is positioned. If electrically conductive materials 118 and 120 arenot associated with their respective substrates, then sealing member 122preferably bonds well to glass. It will be understood that sealingmember 122 can be fabricated from any one of a number of materialsincluding, for example, those disclosed in U.S. Pat. Nos. 4,297,401;4,418,102; 4,695,490; 5,596,023; 5,596,024; and 6,157,480, all of whichare incorporated herein by reference in their entirety.

For purposes of the present disclosure, electrochromic medium 124comprises at least one solvent, an anodic material, a cathodic material,and a current-reducing additive. During normal operation of device 100,the current-reducing additive enables electrochromic medium 124 tooperate at a materially reduced current at a given electrical potential.However, it will be understood that incorporating the current-reducingadditive does not adversely affect the viscosity of the electrochromicmedium to a degree where production rate and/or seal or other devicecomponent failure becomes problematic. Such a viscosity has beenquantitatively determined through production tests to be less thanapproximately 150 centipoise (cP), and preferably less thanapproximately 100 cP, and more preferably less than 50 cP at 20 degreescentigrade. Typically both of the anodic and cathodic materials areelectroactive and at least one of them is electrochromic. It will beunderstood that regardless of its ordinary meaning, the term“electroactive” will be defined herein as a material that undergoes amodification in its oxidation state upon exposure to a particularelectrical potential difference. Additionally, it will be understoodthat the term “electrochromic” will be defined herein, regardless of itsordinary meaning, as a material that exhibits a change in its extinctioncoefficient at one or more wavelengths upon exposure to a particularelectrical potential difference.

Electrochromic medium 124 is preferably chosen from one of the followingcategories:

(1) Single-layer, single-phase:—The electrochromic medium may comprise asingle-layer of material which may include small non-homogenous regionsand includes solution-phase devices where a material may be contained insolution in the ionically conducting electrolyte which remains insolution in the electrolyte when electrochemically oxidized or reduced.Solution phase electroactive materials may be contained in thecontinuous solution-phase of a gel medium in accordance with theteachings of U.S. Pat. No. 5,928,572 entitled “Electrochromic Layer AndDevices Comprising Same” and International Patent Application Serial No.PCT/US98/05570 entitled “Electrochromic Polymeric Solid Films,Manufacturing Electrochromic Devices Using Such Solid Films, AndProcesses For Making Such Solid Films And Devices,” both of which areincorporated herein by reference in their entirety.

More than one anodic and cathodic material can be combined to give apre-selected color as described in U.S. Pat. Nos. 5,998,617, 6,020,987,6,037,471, 6,141,137 and PCT Application Publication No. WO98/44348, allof which are hereby incorporated herein by reference in their entirety.

The anodic and cathodic materials can be combined or linked by abridging unit as described in International Application Serial No.PCT/WO97/30134 entitled “Electrochromic System,” which is incorporatedherein by reference in its entirety. The electrochromic materials canadditionally include near infrared (NIR) absorbing compounds asdescribed in U.S. Pat. No. 6,193,912, which is also incorporated hereinby reference in its entirety.

It is also possible to link anodic materials or cathodic materials bysimilar methods. The concepts described in these applications/patentscan further be combined to yield a variety of electroactive materialsthat are linked or coupled, including linking of a color-stabilizingmoiety to an anodic and/or cathodic material, including those disclosedin U.S. Pat. No. 6,188,505 B1 entitled “Color-Stabilized ElectrochromicDevices,” which is incorporated herein by reference in its entirety.

The anodic and cathodic electrochromic materials can also includecoupled materials as described in U.S. Pat. No. 6,249,369 entitled“Coupled Electrochromic Compounds With Photostable Oxidation States,”which is hereby incorporated herein by reference in its entirety.

The concentration of the electrochromic materials can be selected astaught in U.S. Pat. No. 6,137,620 entitled “Electrochromic Media WithConcentration Enhanced Stability, Process For The Preparation Thereof,and Use In Electrochromic Devices,” the entirety of which is herebyincorporated herein by reference.

Additionally, a single-layer, single-phase medium may include a mediumwhere the anodic and cathodic materials are incorporated into a polymermatrix as is described in International Application Serial No.PCT/W099/02621 entitled “Electrochromic Polymer System” andInternational Patent Application Serial No. PCT/US98/05570 entitled“Electrochromic Polymeric Solid Films, Manufacturing ElectrochromicDevices Using Such Solid Films, And Processes For Making Such SolidFilms And Devices.”

(2) Multi-layer—the medium may be made up in layers and includes amaterial attached directly to an electrically conducting electrode orconfined in close proximity thereto which remains attached or confinedwhen electrochemically oxidized or reduced.

(3) Multi-layer—one or more materials in the medium undergoes a changein phase during the operation of the device, for example a materialcontained in solution in the ionically conducting electrolyte forms alayer on the electrically conducting electrode when electrochemicallyoxidized or reduced.

In addition, electrochromic medium 124 may comprise other materials,such as light absorbers, light stabilizers, thermal stabilizers,antioxidants, tint providing agents, redox buffers, and mixturesthereof. Suitable UV-stabilizers may include: the materialethyl-2-cyano-3,3-diphenyl acrylate, sold by BASF of Parsippany, N.Y.,under the trademark Uvinul N-35 and by Aceto Corp., of Flushing, N.Y.,under the trademark Viosorb 910; the material(2-ethylhexyl)-2-cyano-3,3-diphenyl acrylate, sold by BASF under thetrademark Uvinul N-539; the material2-(2′-hydroxy-4′-methylphenyl)benzotriazole, sold by Ciba-Geigy Corp.under the trademark Tinuvin P; the material3-[3-(2H-benzotriazole-2-yl)-5-(1,1-dimethylethyl)-4-hydroxyphenyl]propionicacid pentyl ester prepared from Tinuvin 213, sold by Ciba-Geigy Corp.,via transesterification or conventional hydrolysis followed byconventional esterification (hereinafter “Tinuvin PE”); the material2,4-dihydroxybenzophenone sold by, among many others, Aldrich ChemicalCo.; the material 2-hydroxy-4-methoxybenzophenone sold by AmericanCyanamid under the trademark Cyasorb UV 9; and the material2-ethyl-2′-ethoxyalanilide sold by Sandoz Color & Chemicals under thetrademark Sanduvor VSU—to name a few.

The anodic material may include, for example, ferrocene, substitutedferrocenes, substituted ferrocenyl salts, substituted phenazines,phenothiazine, substituted phenothiazines, thianthrene, substitutedthianthrenes. Examples of anodic materials may includedi-tert-butyl-diethylferrocene, 5,10-dimethyl-5,10-dihydrophenazine,3,7,10-trimethylphenothiazine, 2,3,7,8-tetramethoxythianthrene, and10-methylphenothiazine. It is also contemplated that the anodic materialmay comprise a polymer film, such as polyaniline, polythiophenes,polymeric metallocenes, or a solid transition metal oxide, including,but not limited to, oxides of vanadium, nickel, iridium, as well asnumerous heterocyclic compounds, etcetera. It will be understood thatnumerous other anodic materials are contemplated for use including thosedisclosed in U.S. Pat. No. 4,902,108 entitled “Single-Compartment,Self-Erasing, Solution-Phase Electrochromic Devices, Solutions For UseTherein, And Uses Thereof,” which is incorporated herein by reference inits entirety, as well as previously referenced and incorporated U.S.Pat. No. 6,188,505 B1.

The cathodic material may include, for example, viologens, such asmethyl viologen tetrafluoroborate, octyl viologen tetrafluoroborate, orbenzyl viologen tetrafluoroborate. It will be understood that thepreparation and/or commercial availability for each of theabove-identified cathodic materials is well known in the art. Whilespecific cathodic materials have been provided, for illustrativepurposes only, numerous other conventional cathodic materials arelikewise contemplated for use including, but by no means limited to,those disclosed in previously referenced and incorporated U.S. Pat. No.4,902,108. Indeed, the only contemplated limitation relative to thecathodic material is that it should not adversely affect theelectrochromic performance of the device 100. Moreover, it iscontemplated that the cathodic material may comprise a polymer film,such as various substituted polythiophenes, polymeric viologens, aninorganic film, or a solid transition metal oxide, including, but notlimited to, tungsten oxide.

For illustrative purposes only, the concentration of the anodic andcathodic materials can range from approximately 1 mM to approximately500 mM and more preferably from approximately 2 mM to approximately 100mM. While particular concentrations of the anodic as well as cathodicmaterials have been provided, it will be understood that the desiredconcentration may vary greatly depending upon the geometricconfiguration of the chamber containing electrochromic medium 124.

For purposes of the present disclosure, the solvent of electrochromicmedium 124 may comprise any one of a number of common, commerciallyavailable solvents including 3-methylsulfolane, dimethyl sulfoxide,dimethyl formamide, acetonitrile, tetraglyme and other polyethers,alcohols such as ethoxyethanol, nitrites, such as glutaronitrile,3-hydroxypropionitrile, 2-methylglutaronitrile, ketones including2-acetylbutyrolactone, cyclopentanone, cyclic esters includingbeta-propiolactone, gamma-butyrolactone, gamma-valerolactone, propylenecarbonate, ethylene carbonate and homogenous mixtures of the same. Whilespecific solvents have been disclosed as being associated with theelectrochromic medium, numerous other solvents that would be known tothose having ordinary skill in the art having the present disclosurebefore them are likewise contemplated for use.

In accordance with the present invention, one or more current-reducingadditive(s) are associated with electrochromic medium 124, which, amongother things, enable the electrochromic medium to operate at a reducedcurrent and/or cell spacing without unduly increasing the viscosity ofthe electrochromic medium. For purposes of the present invention, thecurrent-reducing additives may generally comprise any one of a number ofpolymers including, polyamides, polyimides, polycarbonates, polyesters,polyethers, polymethylmethacrylates, polymethacrylates, polyacrylates,polysilanes, polysiloxanes, polyvinylacetates, polyacrylnitriles,polyvinylalcohols, and combinations thereof.

In a first embodiment of the present invention, the current-reducingadditive may comprise at least one polymer based on polymerization of amaterial represented by formula I:

wherein R₁₋₄ are the same or different and comprise H, a halide, ahydroxy group, a cyano group, an isocyano group, an isothiocyano group,a substituted or unsubstituted and straight or branched alkyl,cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl,alkoxy, alkenyl, or alkynyl group containing approximately 1 toapproximately 40 carbon atom(s), carbonyls, esters, carbonates, amides,ketenes, epoxides, a silyl or siloxyl group containing approximately 1to approximately 40 silicon atom(s), and combinations thereof, whereinthe average molecular weight of the current-reducing additive is greaterthan approximately 1,000 Daltons, and preferably ranges fromapproximately 1,000 to approximately 85,000 Daltons, and more preferablyranges from approximately 1,500 to approximately 50,000 Daltons.

In this embodiment, the current-reducing additive may comprisepolymethylmethacrylate (hereinafter “PMMA”), or a co-polymer of MMA andethyl acrylate which is also known as PMMA/PEA copolymer.

In a second embodiment of the present invention, the current-reducingadditive may comprise at least one polymer based on polymerization of amaterial represented by formula II:

wherein R₅₋₈ are the same or different and comprise H, a halide, ahydroxy group, a cyano group, an isocyano group, an isothiocyano group,a substituted or unsubstituted and straight or branched alkyl,cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl,alkoxy, alkenyl, or alkynyl group containing approximately 1 toapproximately 40 carbon atom(s), carbonyls, esters, carbonates, amides,ketenes, epoxides, a silyl or siloxyl group containing approximately 1to approximately 40 silicon atom(s), and combinations thereof, whereinthe average molecular weight of the current-reducing additive is greaterthan approximately 1,000 Daltons, and preferably ranges fromapproximately 1,000 to approximately 125,000 Daltons, and morepreferably ranges from approximately 1,500 to approximately 50,000Daltons.

In this embodiment, the current-reducing additive may comprise, forexample, polyvinylacetate (hereinafter “PVA”).

In a third embodiment of the present invention, the current-reducingadditive may comprise at least one polymer represented by formula III:

wherein R₉ comprises a substituted or unsubstituted and straight orbranched alkyl, cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl,alkaryl, aralkyl, alkoxy, alkenyl, or alkynyl group containingapproximately 1 to approximately 40 carbon atom(s), carbonyls, esters,carbonates, amides, ketenes, epoxides, a silyl or siloxyl groupcontaining approximately 1 to approximately 40 silicon atom(s), andcombinations thereof, wherein n is an integer which ranges in value from0 to approximately 1,700, wherein the average molecular weight of thecurrent-reducing additive is greater than approximately 1,000 Daltons,and preferably ranges from approximately 1,000 to approximately 125,000Daltons, and more preferably ranges from approximately 1,500 toapproximately 50,000 Daltons.

In a fourth embodiment of the present invention, the current-reducingadditive may comprise at least one polymer represented by formula IV:

wherein R₁₀₋₁₁ are the same or different and comprise a substituted orunsubstituted and straight or branched alkyl, cycloalkyl,polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl, alkoxy,alkenyl, or alkynyl group containing approximately 1 to approximately 40carbon atom(s), carbonyls, esters, carbonates, amides, ketenes,epoxides, a silyl or siloxyl group containing approximately 1 toapproximately 40 silicon atom(s), and combinations thereof, wherein n isan integer which ranges in value from 0 to approximately 1,100, whereinthe average molecular weight of the current-reducing additive is greaterthan approximately 1,000 Daltons, and preferably ranges fromapproximately 1,000 to approximately 125,000 Daltons, and morepreferably from approximately 1,500 to approximately 50,000 Daltons.

In a fifth embodiment of the present invention, the current-reducingadditive may comprise at least one polymer based on formula V:

wherein R₁₂₋₁₅ are the same or different and comprise H, a halide, ahydroxy group, a cyano group, an isocyano group, an isothiocyano group,a substituted or unsubstituted and straight or branched alkyl,cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl,alkoxy, alkenyl, or alkynyl group containing approximately 1 toapproximately 40 carbon atom(s), carbonyls, esters, carbonates, amides,ketenes, epoxides, a silyl or siloxyl group containing approximately 1to approximately 40 silicon atom(s), and combinations thereof, wherein mis an integer which ranges in value from 0 to approximately 500, whereinn is an integer which ranges in value from 1 to approximately 20,wherein the average molecular weight of the current-reducing additive isgreater than approximately 1,000 Daltons, and preferably ranges fromapproximately 1,000 to approximately 125,000 Daltons, and morepreferably ranges from approximately 1,500 to approximately 50,000Daltons.

Preferably the concentration of the above-identified current-reducingadditives range from approximately 5% by weight to approximately 75% byweight, and more preferably from approximately 8% by weight toapproximately 30% by weight.

It will be understood that the current-reducing additives of the presentinvention may comprise polymers, copolymers which may be random oralternating and/or block or grafted in nature, or a hybrid of both. Itwill be further understood that numerous other polymer configurationsthat would be known to those with ordinary skill in the art having thepresent disclosure before them are likewise contemplated for use.

Electrochromic devices having as a component part an electrochromicmedium comprising one or more current-reducing additives can be used ina wide variety of applications wherein the transmitted or reflectedlight can be modulated. Such devices include rear-view mirrors forvehicles; windows for the exterior of a building, home or vehicle;skylights for buildings including tubular light filters; windows inoffice or room partitions; display devices; contrast enhancement filtersfor displays; light filters for photographic devices and light sensors;and indicators for power cells as well as primary and secondaryelectrochemical cells.

In support of the present invention, several experiments were conductedwherein electrochromic devices were prepared which comprised one or morecurrent-reducing additives, the operating current of which were directlycompared to analogous devices filled with different concentrations ofthe same current-reducing additive(s). It will be understood that thecurrent-reducing additives are commercially available from AldrichChemical Co. of Milwaukee, Wis., Inolex Chemical Co. of Philadelphia,Pa., and/or other commercial chemical vendors.

In each one of the experiments below, a series of electrochromic deviceswere filled via conventional vacuum backfilling techniques. Inparticular, each one of the electrochromic devices included a first 2×5inch substrate coated with generally clear, conductive fluorine-dopedtin oxide on the rear surface (112B), and a second 2×5 inch substratecoated with generally clear, conductive fluorine-doped tin oxide on thefront surface (114A) and a standard silver reflector on the rear surface(114B). The two substrates were spaced 137 microns apart foraccommodating the medium.

Experiment No. 1

In experiment No. 1, the electrochromic medium was prepared by mixingthe following materials together in the concentrations provided below:

Component Material Concentration Cathodic Octylviologen [BF₄]₂ 38.0 mMAnodic 5,10-Dimethyl-5, 27.0 mM 10-dihydrophenazine Current-ReducingPMMA (350,000 Daltons) 0, 3, and 5% by wt. Additive Solvent Propylenecarbonate —

Current for each one of the mirrors containing media from experiment No.1 was measured at an electrical potential of 1.2 volts at a steady statecondition using conventional techniques, the results of which areprovided in FIG. 2. As is shown in FIG. 2, increasing the concentrationof the PMMA additive, having an average molecular weight ofapproximately 350,000 Daltons, from 0 to 5% by weight, modestly reducedthe current without adversely affecting the reflective properties of theelectrochromic medium. However, because the viscosity of mediacontaining the high molecular weight PMMA additive was so great, vacuumbackfilling the electrochromic device with a medium having a greateradditive concentration was not possible using conventional devicecomponents. As such, larger reductions in current were not obtainable.It was also noted that dependence of the mirror reflectance on appliedvoltage was identical for each polymer loading concentration.

Experiment No. 2

In experiment No. 2, the electrochromic medium was prepared by mixingthe following materials together in the concentrations provided below:

Component Material Concentration Cathodic Octylviologen [BF₄]₂ 38.0 mMAnodic 5,10-Dimethyl-5,10- 27.0 mM dihydrophenazine Current-ReducingPMMA (12,000 Daltons) 0, 5, 10, and 15% Additive by wt. SolventPropylene carbonate —

Current for each one of the mirrors containing media from experiment No.2 was measured at an electrical potential of 1.2 volts at a steady statecondition using conventional techniques, the results of which areprovided in FIG. 3. As is shown in FIG. 3, increasing the concentrationof the PMMA additive, having an average molecular weight ofapproximately 12,000 Daltons, from 0 to 15% by weight, materiallyreduced the current approximately 65% without adversely affecting thereflective properties of the electrochromic medium. It was also notedthat dependence of the mirror reflectance on applied voltage wasidentical for each polymer loading concentration.

Experiment No. 3

In experiment No. 3, the electrochromic medium was prepared by mixingthe following materials together in the concentrations provided below:

Component Material Concentration Cathodic Octylviologen [BF₄]₂ 38.0 mMAnodic 5,10-Dimethyl-5, 27.0 mM 10-dihydrophenazine Current-Reducing PVA(12,800 Daltons) 0, 3, 5, 10, 15, and Additive 25% by wt. SolventPropylene carbonate —

Current for each one of the mirrors containing media from experiment No.3 was measured at an electrical potential of 1.2 volts at a steady statecondition using conventional techniques, the results of which areprovided in FIG. 4. As is shown in FIG. 4, increasing the concentrationof the PVA additive, having an average molecular weight of approximately12,800 Daltons, from 0 to 25% by weight, materially reduced the currentapproximately 65% without adversely affecting the reflective propertiesof the electrochromic medium. It was also noted that dependence of themirror reflectance on applied voltage was identical for each polymerloading concentration.

Experiment No. 4

In experiment No. 4, the electrochromic medium was prepared by mixingthe following materials together in the concentrations provided below:

Component Material Concentration Cathodic Octylviologen [BF₄]₂ 38.0 mMAnodic 5,10-Dimethyl-5, 27.0 mM 10-dihydrophenazine Current-ReducingLexorez 1931-50* 0, 3, 5, 10, 15, 25, Additive (2,000 Daltons) and 50%by wt. Solvent Propylene carbonate — *Lexorez 1931-50 is commerciallyavailable from Inolex Chemical Co.

Current for each one of the mirrors containing media from experiment No.5 was measured at an electrical potential of 1.2 volts at a steady statecondition using conventional techniques, the results of which areprovided in FIG. 5. As is shown in FIG. 5, increasing the concentrationof the Lexorez additive, having an average molecular weight ofapproximately 2,000 Daltons, from 0 to 50% by weight, materially reducedthe current approximately 90% without adversely affecting the reflectiveproperties of the electrochromic medium. It was also noted thatdependence of the mirror reflectance on applied voltage was identicalfor each polymer loading concentration.

As can be seen from many of the above-provided experiments, theincorporation of one or more of the disclosed current-reducing additivesinto an electrochromic medium materially reduces the operating currentof an associated electrochromic device, and as will be explained below,the relatively low viscosity of the electrochromic medium facilitatesacceptable production rates without a problematic degree of seal orother device component failure.

In further support of the present invention, the viscosity of several ofthe above-identified current-reducing additives was measured using aconventional Brookfield DV II viscometer. The results are provided inTable I.

TABLE I Current- Reducing % MW Temperature Centipoise CentistokesAdditive Wt/Wt (Daltons) (C.) (cP) (cS) PMMA 3 350,000 21 31 26.1 PMMA 5350,000 20.4 428 359.7 PMMA 11.2 120,000 19.6 297 249.6 PMMA/ 11.2101,000 20.4 204 171.4 PEA PVA 10 100,000 19.6 80 67.2 PVA 10 12,80020.4 9 7.6 PVA 15 12,800 20.4 34 28.6

As can be seen from Table I, among other things, the 350,000 Dalton PMMAloaded to a concentration of only 5% is commercially undesirable becauseof its enormous viscosity. However, the 101,000 Dalton PMMA/PEAco-polymer loaded to a concentration of 11.2%, the 100,000 Dalton PVAloaded to a concentration of 10%, and the 12,800 Dalton PVA loaded to aconcentration of 15% exhibit desirable viscosities which will facilitateacceptable production rates without a problematic degree of seal orother device component failure, and, as was shown in experiments 1–4,such large loading concentrations of the current-reducing additive willmaterially reduce current of an associated device, and/or allow forreduced cell spacing while maintaining a substantially unchangedcurrent. Moreover, FIG. 6 of the present invention clearly shows, amongother things, that the 350,000 Dalton PMMA exhibits a viscosity of over1,500 cP at a loading of less than 10% by weight; by comparison the12,800 Dalton PVA exhibits a viscosity of only 91 cP at a loading of 30%by weight.

While the invention has been described in detail herein in accordancewith certain preferred embodiments thereof, many modifications andchanges therein may be effected by those skilled in the art.Accordingly, it is our intent to be limited only by the scope of theappending claims and not by way of details and instrumentalitiesdescribing the embodiments shown herein.

1. An electrochromic medium for use in an electrochromic device,comprising: at least one solvent; an anodic electroactive material; acathodic electroactive material, wherein at least one of the anodic andcathodic electroactive materials is electrochromic; a current-reducingadditive, wherein the current-reducing additive comprises a polymerpresent in an effective concentration to reduce the current of theelectrochromic medium upon application of an electrical potential by atleast approximately 20% relative to an electrochromic medium without thecurrent-reducing additive; and wherein the electrochromic mediumcomprises a cross-linked polymer matrix.
 2. The electrochromic mediumaccording to claim 1, wherein the average molecular weight of thecurrent-reducing additive is greater than approximately 1,000 Daltons.3. The electrochromic medium according to claim 1, wherein the averagemolecular weight of the current-reducing additive ranges fromapproximately 1,500 Daltons to approximately 125,000 Daltons.
 4. Theelectrochromic medium according to claim 1, wherein the averagemolecular weight of the current-reducing additive ranges fromapproximately 1,500 Daltons to approximately 50,000 Daltons.
 5. Theelectrochromic medium according to claim 1, wherein the current-reducingadditive is present in a concentration ranging from approximately 5% byweight to approximately 75% by weight.
 6. The electrochromic mediumaccording to claim 1, wherein the current-reducing additive is presentin a concentration ranging from approximately 8% by weight toapproximately 30% by weight.
 7. The electrochromic medium according toclaim 1, wherein the current-reducing additive is selected from thegroup comprising polyamides, polyimides, polycarbonates, polyesters,polyethers, polymethacrylates, polyacrylates, polysilanes,polysiloxanes, polyvinylacetates, polyacrylonitriles, polyvinylalcohols,and combinations thereof.
 8. The electrochromic medium according toclaim 1, wherein the current-reducing additive is present in aneffective concentration to reduce the current of the electrochromicmedium upon application of an electrical potential by at leastapproximately 40% relative to an electrochromic medium without thecurrent-reducing additive.
 9. An electrochromic device, comprising: afirst substantially transparent substrate having an electricallyconductive material associated therewith; a second substrate having anelectrically conductive material associated therewith; and theelectrochromic medium according to claim 1 contained within a chamberpositioned between the first and second substrates.
 10. Theelectrochromic device according to claim 9, wherein the device is anelectrochromic window.
 11. The electrochromic device according to claim9, wherein the second substrate is coated with a reflective material.12. The electrochromic device according to claim 9, wherein a firstsurface of the second substrate is coated with a reflective material.13. The electrochromic device according to claim 12, wherein the deviceis an electrochromic mirror.
 14. An electrochromic medium for use in anelectrochromic device, comprising: at least one solvent; an anodicelectroactive material; a cathodic electroactive material, wherein atleast one of the anodic and cathodic electroactive materials iselectrochromic; a current-reducing additive, wherein thecurrent-reducing additive is present in a concentration greater than 12%by weight; and wherein the electrochromic medium comprises across-linked polymer matrix.
 15. The electrochromic medium according toclaim 14, wherein the current-reducing additive is present in aconcentration greater than 15% by weight.
 16. An electrochromic device,comprising: a first substantially transparent substrate having anelectrically conductive material associated therewith; a secondsubstrate having an electrically conductive material associatedtherewith; and the electrochromic medium according to claim 14 containedwithin a chamber positioned between the first and second substrates. 17.The electrochromic device according to claim 16, wherein the device isan electrochromic window.
 18. The electrochromic device according toclaim 16, wherein the second substrate is coated with a reflectivematerial.
 19. The electrochromic device according to claim 16, wherein afirst surface of the second substrate is coated with a reflectivematerial.
 20. The electrochromic device according to claim 19, whereinthe device is an electrochromic mirror.
 21. An electrochromic medium foruse in an electrochromic device, comprising: at least one solvent; ananodic electroactive material; a cathodic electroactive material,wherein at least one of the anodic and cathodic electroactive materialsis electrochromic; a current-reducing additive, wherein thecurrent-reducing additive comprises at least one polymer based onpolymerization of a material represented by formula I:

 wherein R₁₋₄ are the same or different and comprise H, a halide, ahydroxy group, a cyano group, an isocyano group, an isothiocyano group,a substituted or unsubstituted and straight or branched alkyl,cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl,alkoxy, alkenyl, or alkynyl group containing approximately 1 toapproximately 40 carbon atom(s), carbonyls, esters, carbonates, amides,ketenes, epoxides, a silyl or siloxyl group containing approximately 1to approximately 40 silicon atom(s), and combinations thereof; whereinthe current-reducing additive is present in an effective concentrationto materially reduce the current of the electrochromic medium uponapplication of an electrical potential relative to an electrochromicmedium without the current-reducing additive; wherein thecurrent-reducing additive comprises an average molecular weight of lessthan approximately 85,000 Daltons; and wherein the electrochromic mediumcomprises a cross-linked polymer matrix.
 22. An electrochromic device,comprising: a first substantially transparent substrate having anelectrically conductive material associated therewith; a secondsubstrate having an electrically conductive material associatedtherewith; and the electrochromic medium according to claim 21 containedwithin a chamber positioned between the first and second substrates. 23.The electrochromic device according to claim 22, wherein the device isan electrochromic window.
 24. The electrochromic device according toclaim 22, wherein the second substrate is coated with a reflectivematerial.
 25. The electrochromic device according to claim 22, wherein afirst surface of the second substrate is coated with a reflectivematerial.
 26. The electrochromic device according to claim 25, whereinthe device is an electrochromic mirror.
 27. An electrochromic medium foruse in an electrochromic device, comprising: at least one solvent; ananodic electroactive material; a cathodic electroactive material,wherein at least one of the anodic and cathodic electroactive materialsis electrochromic; a current-reducing additive, wherein thecurrent-reducing additive comprises at least one polymer based onpolymerization of a material represented by formula II:

 wherein R₅₋₈ are the same or different and comprise H, a halide, ahydroxy group, a cyano group, an isocyano group, an isothiocyano group,a substituted or unsubstituted and straight or branched alkyl,cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl,alkoxy, alkenyl, or alkynyl group containing approximately 1 toapproximately 40 carbon atom(s), carbonyls, esters, carbonates, amides,ketenes, epoxides, a silyl or siloxyl group containing approximately 1to approximately 40 silicon atom(s), and combinations thereof; andwherein the current-reducing additive is present in an effectiveconcentration to materially reduce the current of the electrochromicmedium upon application of an electrical potential relative to anelectrochromic medium without the current-reducing additive; and whereinthe electrochromic medium comprises a cross-linked polymer matrix. 28.An electrochromic device, comprising: a first substantially transparentsubstrate having an electrically conductive material associatedtherewith; a second substrate having an electrically conductive materialassociated therewith; and the electrochromic medium according to claim27 contained within a chamber positioned between the first and secondsubstrates.
 29. The electrochromic device according to claim 28, whereinthe device is an electrochromic window.
 30. The electrochromic deviceaccording to claim 28, wherein the second substrate is coated with areflective material.
 31. The electrochromic device according to claim28, wherein a first surface of the second substrate is coated with areflective material.
 32. The electrochromic device according to claim31, wherein the device is an electrochromic mirror.
 33. Anelectrochromic medium for use in an electrochromic device, comprising:at least one solvent; an anodic electroactive material; a cathodicelectroactive material, wherein at least one of the anodic and cathodicelectroactive materials is electrochromic; a current-reducing additive,wherein the current-reducing additive comprises at least one polymerrepresented by formula III:

 wherein R₉ comprises a substituted or unsubstituted and straight orbranched alkyl, cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl,alkaryl, aralkyl, alkoxy, alkenyl, or alkynyl group containingapproximately 1 to approximately 40 carbon atom(s), carbonyls, esters,carbonates, amides, ketenes, epoxides, a silyl or siloxyl groupcontaining approximately 1 to approximately 40 silicon atom(s), andcombinations thereof, wherein n is an integer which ranges in value from0 to approximately 1,700; and wherein the current-reducing additive ispresent in an effective concentration to materially reduce the currentof the electrochromic medium upon application of an electrical potentialrelative to an electrochromic medium without the current-reducingadditive; and wherein the electrochromic medium comprises a cross-linkedpolymer matrix.
 34. An electrochromic device, comprising: a firstsubstantially transparent substrate having an electrically conductivematerial associated therewith; a second substrate having an electricallyconductive material associated therewith; and the electrochromic mediumaccording to claim 33 contained within a chamber positioned between thefirst and second substrates.
 35. The electrochromic device according toclaim 34, wherein the device is an electrochromic window.
 36. Theelectrochromic device according to claim 34, wherein the secondsubstrate is coated with a reflective material.
 37. The electrochromicdevice according to claim 34, wherein a first surface of the secondsubstrate is coated with a reflective material.
 38. The electrochromicdevice according to claim 37, wherein the device is an electrochromicmirror.
 39. An electrochromic medium for use in an electrochromicdevice, comprising: at least one solvent; an anodic electroactivematerial; a cathodic electroactive material, wherein at least one of theanodic and cathodic electroactive materials is electrochromic; acurrent-reducing additive, wherein the current-reducing additivecomprises at least one polymer represented by formula IV:

 wherein R₁₀₋₁₁ are the same or different and comprise a substituted orunsubstituted and straight or branched alkyl, cycloalkyl,polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl, alkoxy,alkenyl, or alkynyl group containing approximately 1 to approximately 40carbon atom(s), carbonyls, esters, carbonates, amides, ketenes,epoxides, a silyl or siloxyl group containing approximately 1 toapproximately 40 silicon atom(s), and combinations thereof, wherein n isan integer which ranges in value from 0 to approximately 1,100; andwherein the current-reducing additive is present in an effectiveconcentration to materially reduce the current of the electrochromicmedium upon application of an electrical potential relative to anelectrochromic medium without the current-reducing additive; and whereinthe electrochromic medium comprises a cross-linked polymer matrix. 40.An electrochromic device, comprising: a first substantially transparentsubstrate having an electrically conductive material associatedtherewith; a second substrate having an electrically conductive materialassociated therewith; and the electrochromic medium according to claim39 contained within a chamber positioned between the first and secondsubstrates.
 41. The electrochromic device according to claim 40, whereinthe device is an electrochromic window.
 42. The electrochromic deviceaccording to claim 40, wherein the second substrate is coated with areflective material.
 43. The electrochromic device according to claim40, wherein a first surface of the second substrate is coated with areflective material.
 44. The electrochromic device according to claim43, wherein the device is an electrochromic mirror.
 45. Anelectrochromic medium for use in an electrochromic device, comprising:at least one solvent; an anodic electroactive material; a cathodicelectroactive material, wherein at least one of the anodic and cathodicelectroactive materials is electrochromic; a current-reducing additive,wherein the current-reducing additive comprises at least one polymerbased on formula V:

 wherein R₁₂₋₁₅ are the same or different and comprise H, a halide, ahydroxy group, a cyano group, an isocyano group, an isothiocyano group,a substituted or unsubstituted and straight or branched alkyl,cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl,alkoxy, alkenyl, or alkynyl group containing approximately 1 toapproximately 40 carbon atom(s), carbonyls, esters, carbonates, amides,ketenes, epoxides, a silyl or siloxyl group containing approximately 1to approximately 40 silicon atom(s), and combinations thereof, wherein mis an integer which ranges in value from 0 to approximately 500, whereinn is an integer which ranges in value from 1 to approximately 20; andwherein the current-reducing additive is present in an effectiveconcentration to materially reduce the current of the electrochromicmedium upon application of an electrical potential relative to anelectrochromic medium without the current-reducing additive; and whereinthe electrochromic medium comprises a cross-linked polymer matrix. 46.An electrochromic device, comprising: a first substantially transparentsubstrate having an electrically conductive material associatedtherewith; a second substrate having an electrically conductive materialassociated therewith; and the electrochromic medium according to claim45 contained within a chamber positioned between the first and secondsubstrates.
 47. The electrochromic device according to claim 46, whereinthe device is an electrochromic window.
 48. The electrochromic deviceaccording to claim 46, wherein the second substrate is coated with areflective material.
 49. The electrochromic device according to claim46, wherein a first surface of the second substrate is coated with areflective material.
 50. The electrochromic device according to claim49, wherein the device is an electrochromic mirror.
 51. Anelectrochromic medium for use in an electrochromic device, comprising:at least one solvent; an anodic electroactive material; a cathodicelectroactive material, wherein at least one of the anodic and cathodicelectroactive materials is electrochromic; a cross-linked polymermatrix; and a current-reducing additive, wherein the current-reducingadditive is selected from at least one of the group consisting of: (1)at least one polymer based on polymerization of a material representedby formula I:

 wherein R₁₋₄ are the same or different and comprise H, a halide, ahydroxy group, a cyano group, an isocyano group, an isothiocyano group,a substituted or unsubstituted and straight or branched alkyl,cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl,alkoxy, alkenyl, or alkynyl group containing approximately 1 toapproximately 40 carbon atom(s), carbonyls, esters, carbonates, amides,ketenes, epoxides, a silyl or siloxyl group containing approximately 1to approximately 40 silicon atom(s), and combinations thereof; whereinthe current-reducing additive is present in an effective concentrationto materially reduce the current of the electrochromic medium uponapplication of an electrical potential relative to an electrochromicmedium without the current-reducing additive; and wherein thecurrent-reducing additive comprises an average molecular weight of lessthan approximately 85,000 Daltons; (2) at least one polymer based onpolymerization of a material represented by formula II:

 wherein R₅₋₈ are the same or different and comprise H, a halide, ahydroxy group, a cyano group, an isocyano group, an isothiocyano group,a substituted or unsubstituted and straight or branched alkyl,cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl,alkoxy, alkenyl, or alkynyl group containing approximately 1 toapproximately 40 carbon atom(s), carbonyls, esters, carbonates, amides,ketenes, epoxides, a silyl or siloxyl group containing approximately 1to approximately 40 silicon atom(s), and combinations thereof; andwherein the current-reducing additive is present in an effectiveconcentration to materially reduce the current of the electrochromicmedium upon application of an electrical potential relative to anelectrochromic medium without the current-reducing additive; (3) atleast one polymer represented by formula III:

 wherein R₉ comprises a substituted or unsubstituted and straight orbranched alkyl, cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl,alkaryl, aralkyl, alkoxy, alkenyl, or alkynyl group containingapproximately 1 to approximately 40 carbon atom(s), carbonyls, esters,carbonates, amides, ketenes, epoxides, a silyl or siloxyl groupcontaining approximately 1 to approximately 40 silicon atom(s), andcombinations thereof, wherein n is an integer which ranges in value from0 to approximately 1,700; and wherein the current-reducing additive ispresent in an effective concentration to materially reduce the currentof the electrochromic medium upon application of an electrical potentialrelative to an electrochromic medium without the current-reducingadditive; (4) at least one polymer represented by formula IV:

 wherein R₁₀₋₁₁ are the same or different and comprise a substituted orunsubstituted and straight or branched alkyl, cycloalkyl,polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl, alkoxy,alkenyl, or alkynyl group containing approximately 1 to approximately 40carbon atom(s), carbonyls, esters, carbonates, amides, ketenes,epoxides, a silyl or siloxyl group containing approximately 1 toapproximately 40 silicon atom(s), and combinations thereof, wherein n isan integer which ranges in value from 0 to approximately 1,100; andwherein the current-reducing additive is present in an effectiveconcentration to materially reduce the current of the electrochromicmedium upon application of an electrical potential relative to anelectrochromic medium without the current-reducing additive; and atleast one polymer represented by formula V:

 wherein R₁₂₋₁₅ are the same or different and comprise H, a halide, ahydroxy group, a cyano group, an isocyano group, an isothiocyano group,a substituted or unsubstituted and straight or branched alkyl,cycloalkyl, polycycloalkyl, heterocycloalkyl, aryl, alkaryl, aralkyl,alkoxy, alkenyl, or alkynyl group containing approximately 1 toapproximately 40 carbon atom(s), carbonyls, esters, carbonates, amides,ketenes, epoxides, a silyl or siloxyl group containing approximately 1to approximately 40 silicon atom(s), and combinations thereof, wherein mis an integer which ranges in value from 0 to approximately 500, whereinn is an integer which ranges in value from 1 to approximately 20; andwherein the current-reducing additive is present in an effectiveconcentration to materially reduce the current of the electrochromicmedium upon application of an electrical potential relative to anelectrochromic medium without the current-reducing additive.